Micromembrane absorber with deep-permeation nanostructure assembled by flowing synthesis

A micromembrane adsorber with deep-permeation nanostructure (DPNS) has been successfully fabricated by flowing synthesis. The nanoparticles are in-situ assembled in membrane pores and immobilized in each membrane pore along the direction of membrane thickness. The nanoparticles with a lower size and thinner size distribution can be achieved owing to the confined space effect of the membrane pores. As a concept-of-proof, the nano ZIF-8 and ZIF-67 are fabricated in porous membrane pores for methyl orange (MO) and rhodamine B (RhB) adsorption. The adsorption rate is increased significantly owing to the enhanced contact and mass transfer in the confined space. The adsorption capacity for the RhB is also increased, since the size of the nanoparticles assembled in membrane pores is smaller with more active sites exposed. This micromembrane adsorber with DPNS has good reusability and can provide a promising prospect for industrial application.     

Precise quantification of the antibacterial activity of chitosan by NB medium neutralizer

In the present research,nutrient broth(NB)medium was identified to be able to neutralize the antibac-terial activity of chitosan and its derivatives.Therefore,an improved test method independent of NB medium was proposed to precisely quantify the antibacterial effectiveness and efficiency of chitosan.The minimum bactericidal concentration(MBC)of chitosan was 60 μg mL-1 against S.aureus and E.coli,and 0.01％(w/v)chitosan could kill 100％of bacteria within 3 min.From another point of view,the neutralizing efficiency of NB could be tripled by adding 25 g L-1 of sodium chloride.Then the neutraliz-ing mechanism of NB medium was ascribed to flocculation between chitosan and protein.Adding extra sodium chloride could significantly reduce the size of floccules,and smaller floccules would lose the ability of binding with bacteria directly,showing higher neutralizing rate on the macro scale.     

氧化铝纤维束织造过程中摩擦磨损性能研究

运用往复线性摩擦试验方法,搭配自制的摩擦试验夹具,模拟织造过程中氧化铝纤维束-筘齿的摩擦行为,研究加载力、预加张力和摩擦频率对悬空状态下氧化铝纤维束摩擦磨损性能的影响.结果表明:随着加载力的增加,氧化铝纤维束所受摩擦力及长丝断裂根数增加,摩擦系数减小;在预加张力为0.40 N时,氧化铝纤维束所受摩擦力和摩擦系数出现最小值,磨损程度也最小;在摩擦稳定阶段,摩擦频率增加,则氧化铝纤维束所受摩擦力先下降,后略有上升,当摩擦频率增加至5 Hz时,氧化铝纤维束的摩擦系数较1 Hz时增加18.7％,磨损程度也最为严重.     

The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

水夹点技术在高校食堂洗菜工艺中的应用

以洗菜工艺为例,利用水夹点技术对某高校中某食堂清洁用水进行分析,实现了生活用水的节水减排目标,节约水量分别占洗菜工艺和全用水过程的65％和28％.     

Phase composition,microstructure and thermophysical properties of the Srx(Zr0.9Y0.05Yb0.05)O1.95+x ceramics

Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x (x=1.0, 0.9, 0.8, 0.7) ceramics were prepared by solid state reaction sintering. The sintered Sr_1.0(Zr_0.9Y_0.05Yb_0.05)O_2.95 is a single-phase solid solution while the sintered Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x (x=0.9?0.7) are composites, and a significant grain growth inhibition is observed in the sintered Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x (x=1.0, 0.9). Rare-earth elements distribution in the bulk materials indicates that Yb and Y preferentially substitute Zr-sites in SrZrO₃, and the highest solubility of RE₂O₃ in pure SrZrO₃ is ～0.8 mol%. The sintered Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x have high thermal expansion coefficients up to ～11.0×10^?6 K^-1 (1200°C). Sr_0.8(Zr_0.9Y_0.05Yb_0.05)O_2.75 has the lowest thermal conductivity of 1.38 W·m^-1·K^-1 at 800°C. Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x (x=1.0, 0.9, 0.8) show no phase transition from 600 to 1400°C, whereas Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x (x=0.9, 0.8) have excellent high-temperature phase stability over the whole investigated temperature range. Therefore, Sr_x(Zr_0.9Y_0.05Yb_0.05)O_1.95+x (x=1.0, 0.9, 0.8) are considered as promising TBCs materials that might be operated at higher temperatures compared to YSZ.     

High energy-storage performance of lead-free AgNbO3 antiferroelectric ceramics fabricated via a facile approach

AgNbO₃ lead free AFE ceramics are considered as one of the promising alternatives to energy storage applications. In the majority of studies concerning the preparation of AgNbO₃ AFE ceramics, an oxygen atmosphere is required to achieve high performance, increasing the complexity of the fabrication process. Herein, a facile approach to preparing AgNbO₃ ceramics in the ambient air was reported, in which the AgNbO₃ ultrafine powder with stable perovskite structure was synthesized by hydrothermal method instead of the conventional ball milling process, leading to a lower temperature of phase formation and thus smaller grain size. The resulting ceramics sintered at 940 °C displayed high breakdown strength (216 kV/cm) and a recoverable energy density of 3.26 J/cm³ with efficiency of 53.5 %. Also, the high thermal stability of recoverable energy density (with minimal variation of ≤20 %) and efficiency (≤ 10 %) over 30–150℃, enables AgNbO₃ ceramics achieved to be a promising candidate for energy storage applications.     

Eco-friendly and degradable red phosphorus nanoparticles for rapid microbial sterilization under visible light

Pathogens pose a serious challenge to environmental sanitation and a threat to public health.The frequent use of chemicals for sterilization in recent years has not only caused secondary damage to the environment but also increased pathogen resistance to drugs,which further threatens public health.To address this issue,the use of non-chemical antibacterial means has become a new trend for environmental disinfection.In this study,we developed red phosphorus nanoparticles(RPNPs),a safe and degradable photosensitive material with good photocatalytic and photothermal properties.The red phosphorus nanoparticles were prepared using a template method and ultrasonication.Under the irradiation of simulated sunlight for 20 min,the RPNPs exhibited an efficiency of 99.98%in killing Staphylococcus aureus due to their excellent photocatalytic and photothermal abilities.Transmission electron microscopy and ultraviolet–visible spectroscopy revealed that the RPNPs exhibited degradability within eight weeks.Both the RPNPs and their degradation products were nontoxic to fibroblast cells.Therefore,such RPNPs are expected to be used as a new type of low-cost,efficient,degradable,biocompatible,and eco-friendly photosensitive material for environmental disinfection.     

Non-Halogenated-Solvent Processed and Additive-Free Tandem Organic Solar Cell with Efficiency Reaching 16.67%

Organic solar cells (OSCs) have recently reached a remarkably high efficiency and become a promising technology for commercial application. However, OSCs with top efficiency are mostly processed by halogenated solvents and with additives that are not environmentally friendly, which hinders large-scale manufacture. In this study, high-performance tandem OSCs, based on polymer donors and two small-molecule acceptors with different bandgaps, are fabricated by solution processing with non-halogenated solvents without additive. Importantly, the two active layers developed from non-halogenated solvents show better phase segregation and charge transport properties, leading to superior performance than halogenated ones. As a result, a tandem OSC with high efficiency of up to 16.67% is obtained, showing unique advantages in future massive production.     

Additive Manufacturing of Stable Energy Storage Devices Using a Multinozzle Printing System

The development of the Internet of things has prompted an exponential increase in the demand for flexible, wearable devices, thereby posing new challenges to their integration and conformalization. Additive manufacturing facilitates the fabrication of complex parts via a single integrated process. Herein, the development of a multinozzle, multimaterial printing device is reported. This device accommodates the various characteristics of printing materials, ensures high-capacity printing, and can accommodate a wide range of material viscosities from 0 to 1000 Cp. Complete capacitors, inclusive of the current collector, electrode, and electrolyte, can be printed without repeated clamping to complete the preheating, printing, and sintering processes. This method addresses the poor stability issue associated with printed electrode materials. Furthermore, after the intercalation of LiFePO₄ with Na ions, X-ray photoelectron spectroscopy and X-ray diffraction results reveal that the Na ions permeate the interlayer structure of LiFePO₄, enhancing the ion migration channels by increasing the ion transmission rate. A current rate of 2.5 mAh ensures >2000 charge/discharge cycles, while retaining a charge/discharge efficiency of 96% and a discharge capacity of 91.3 mAh g⁻¹. This manufacturing process can provide conformal power modules for a diverse range of portable devices with various shapes, improving space utilization.